Precursor compositions for cold cure high resilience foams

ABSTRACT

A composition suitable for use in producing cold cure high resilience polyether urethane foam selected from the class consisting of (I) a composition consisting essentially of a major amount of an organic polyol and a minor amount of a siloxane block copolymer and (II) a composition consisting essentially of a major amount of water, a minor amount of an amine catalyst, a minor amount of an organic surfactant and a minor amount of a siloxane block copolymer.

United States Patent [1 1 Morehouse PRECURSOR COMPOSITIONS FOR COLD CURE HIGH RESILIENCE FOAMS [75] inventor: Edward Lewis Morehouse, New

City, NY.

[73] Assignee: Union Carbide Corporation, New

York, NY.

[22] Filed: Apr. 17, 1973 [21] Appl. No: 351,978

Related US. Application Data [62] Division of Ser. No. 84,181, Oct. 26, 1970, Pat. No.

[52] US. Cl. 252/182; 260/25 Al-l; 260/25 AP; 260/25 AQ; 260/25 BD [51] Int. Cl. C08g 22/46 [58] Field of Search. 252/182; 260/25 AH, 2.5 AP, 260/25 BD, 2.5 AQ

{56] References Cited UNITED STATES PATENTS 3,420,782 11/1969 Dahm 260/25 AH 3,505,377 1/1970 Morehouse 3,507,815 4/1970 Bailey 260/25 AH June 3, 1975.

9/ 1970 Rossmy 3,526,651 260/25 AH 3,560,544 2/1971 l-laluska 260/25 Al-l FOREIGN PATENTS OR APPLICATIONS 1,101,752 8/1959 Germany 260/25 AH 1,081,083 8/ 1967 United Kingdom 260/25 AH 944,904 12/ 1963 United Kingdom 260/25 Al-l 666,545 10/1966 South Africa 1,162,517 8/ 1969 United Kingdom Primary Examiner .Benjamin R. Padgett Assistant Examiner-Irwin Gluck Attorney, Agent, or FirmR. J. Finnegan [57] ABSTRACT 11 Claims, No Drawings PRECURSOR COMPOSITIONS FOR COLD CURE Il-IIGH RESILIENCE FOAMS This application is a divisional of application Ser. No. 84,181 filed October 26, 1970, now US. Pat. No. 3,741,917.

This invention relates to high resilience cold cure polyether urethane foams and more particularly to the use of certain organosilicon surfactants in the production of such foams.

The formation of any urethane foam depends primarily on the reaction between a polyol and an isocyanate in the presence of blowing agents. Most conventional urethane foams are hot cured foams. With hot cured urethane foams, whether slabstock or molded, the rate of reaction and heat generated by the exothermic reaction between the polyol and isocyanate is sufficient to cure the center of the foam piece, but the surface tem perature of the foam usually does not rise sufficiently high enough to cure the outside rapidly. Consequently it is generally necessary to apply some form of external heating to complete the curing rapidly and to eliminate any surface tackiness. The general method is to postcure the foam while in the mold at temperatures of 100C. to 150C. in an infrared oven for about to 30 minutes.

More recently cold cure urethane foams have been developed in an attempt to increase the exothermic temperature of the reaction and generally speed up the entire gellation process. This is accomplished through the use of polyols having a substantial amount of primary hydroxyl groups. Cold cure urethane foam is also referred to as high resilience foam.

This cold cure technology offers may potential and real economic advantages to the manufacture. For example, because of faster cure times the overall processing time is reduced and more foam can be produced per day thus substantially lowering capitol expenditure. Moreover, the properties of cold cure urethane foam unlike hot cured urethane foam are very similar to those of latex foam. In addition, compared to hot cured urethane foam, cold cure urethane foam characteristically provides better resilience, higher SAC factors (i.e., load bearing properties which relate to comfort in cushioning applications), superior flex fatigue and lower flammability.

Because of the high reactivity of cold cure systems, the foams are generally self-stabilizing or very nearly self-stabilizing and can be generally obtained without the use of a stabilizing agent. However, several drawbacks still remain with regard to cold cure technology. For instance, without an agent to control cell size, the cold cure urethane foam structure typically is coarse, often nonuniform and may contain voids; the foam also has a tendency to settle and may even collapse.

It has now been discovered that the above drawbacks can be overcome and that flexible cold cure polyether urethane foams having high resilience can be prepared according to the instant invention which involves employing certain siloxane block copolymer surfactants in conjunction with certain organic polyols are more fully defined below.

This invention is based in part on the discovery that certain low molecular weight siloxane block copolymer surfactants can be used to control the cell uniformity of cold cure polyether urethane foams with little if any form shrinkage and without any severe adverse effect to the foams resilience and its resistence towards flammability. Moreover, voids in the foam are eliminated or at least greatly reduced by this instant invention and the cell structure of the cold cure polyether urethane foam is also much uniform and finer than where no surfactant agent is used.

This discovery is indeed surprising, since not all siloxane block copolymer surfactants can be employed. For instance, relatively high molecular weight siloxane surfactants which are good stabilizers for conventional flexible hot cure urethane foams are not satisfactory for cold cure systems, because they cause foam shrinkage and severe loss in resilience at surfactant levels where there is an improvement in cell structure. Attempts to lower the surfactant concentration of such conventional high molecular weight siloxane surfactants to improve on foam shrinkage merely serve to destroy any gain in improved cell structure possible at the proper level of concentration. Furthermore, far lower foam flammability is obtainable with the specific siloxane block copolymer surfactants of this invention than with the high molecular weight siloxane stabilizers of conventional hot cure flexible foam. In addition, it has also been discovered that crushing of the cold cure urethane foam, a common industrial practice, can extend the usefulness of the siloxane block copolymer surfactants employed in this invention. For example, crushing of the uniform, fine celled, non-shrinking cold cure polyether urethane foams stabilized by the siloxane block copolymer surfactants useful in this invention can result in higher resiliency than that of the corresponding uncrushed foams. In contrast when siloxane block copolymer surfactants having compositions outside of the scope of this invention are used, foam porosities are so low that even the crushed foams are deform severely by shrinkage.

Therefore it is an object of this invention to provide a process for producing cold cure polyether urethane foams. It is another object of this invention to provide compositions suitable for use in producing a uniform, high resilient cold cure polyether urethane foam. Other objects and advantages of this invention will become readily apparent from the following description and appended claims.

More specifically the instant invention is directed, in part, to a process for preparing cold cure polyether urethane foam, said process comprising foaming and reacting a reaction mixture comprising:

I. an organic polyol selected from the group consisting of (A) a polyether triol containing at least 40 mole per cent primary hydroxyl groups and having a molecular weight from about 2,000 to about 8,000 and (B) a mixture of said polyether triol and other polyethers having an average of at least two hydroxyl groups, said polyether triol of said mixture amounting to at least 40 weight per cent of the total polyol content;

II. a polyisocyanate, said organic polyol and said polyisocyanate being present in the mixture in a major amount and in the relative amount required to produce the urethane;

III. a blowing agent in a minor amount sufficient to foam the reaction mixture;

IV. a catalytic amount of a catalyst for the production of the urethane from the organic polyol and polyisocyanate; and

V. a minor amount of a siloxane block copolymer surfactant having a molecular weight from about 500 to about 4,000, a siloxane content from about 25 to about 90 weight per cent based on the weight of the copolymer and an oxyethylene content of at least 35 weight per cent based on the total amount of any oxyalkylene groups present in said copolymer.

It is to be understood of course that the above process and the appended claims read on employing a single ingredient of the type specified or any of the various combinations of ingredient mixtures possible. For example, in addition to employing a single ingredient of the types specified, if desired, a mixture of triols, a mixture of polyisocyanates, a mixture of blowing agents, a mixture of catalysts and/or a mixture of siloxane block copolymers can be employed. Likewise the triolby R are rnonovalent hydrocarbon radicals.

Illustrative of the monovalent hydrocarbon groups that are represented by R in formula (I) are alkyl groups (for example, methyl, ethyl, isopropyl, octyl, dodecyl, octadecyl, eicosyl and the like); alkenyl groups (for example, vinyl, ally] and the like); cycloalkenyl groups (for example, cyclohexenyl and the like); aryl groups (for example, phenyl, naphthyl and the like); aralkyl groups (for example, benzyl, phenylethyl and the like); alkaryl groups (for example, tolyl, n-hexylphenyl and the like); and cycloalkyl groups (for example, cyclohexyl and the like). If desired such groups can contain substituents such as halogens and the like. Preferably said hydrocarbon radicals contain polyether starting mixture could consist of a single triol f one to carbon atoms, and a mixture Of polyethers, a mixture Of tX'iOlS and a The tructure of the divalent rganic group represingle polyether or a mixture of two or more triols and Sented by in f l (I) is dependent upon the type two Or more p y of reaction involved in producing the siloxane block As indicated above, the siloxane block copolymers copolymer Such copolymers can b produced b any employed as surfactants in this invention are character- 20 number of reactions thereby giving rise to a variety of ized by certain molecular weights, siloxane contents divalent organic groups linking the siloxane portion to and oxyethylene contents. Provided that the copolythe R'-(R"),,X portion of the copolymer. The promers conform to these limitations, they may have any cesses involve reacting a siloxane with an organic comof a wide variety of structures and substituents and still pound such as alcohols, polyethers, olefinically unsatube effective in this invention. Subject to this qualification, a more detailed description of some of the useful rated compounds, and the like. Typical of such reactions are the following:

siloxane block polymers is presented below.

The siloxane block copolymers that are useful in this invention are those copolymers having siloxane portions (or blocks) composed essentially of siloxane groups represented by the formula:

(I) wherein b has a value of 1 to 3 inclusive and R is a monovalent hydrocarbon group or a -R-(R) X group which R is divalent organic group linked directly to the silicon atom, R" is an oxyalkylene group, X is a monovalent organic terminating group and n is O or an integer. The groups represented by R, R, R" and X and the values of n and b can be the same or different in any given group, block or portion of the copolymer, However each siloxane portion of the copolymer must contain (l) at least one group represented by formula (I) wherein at least one group represented by R is a R (R"-),, X group and (2) at least one group represented by formula I wherein b is 2 and both groups represented In the above equations (a) to (0), R represents a monovalent hydrocarbon radical, preferably an alkyl or aryl group, X represents a halogen atom or amino group such as NI I NI-IR and NR wherein R is a monovalent hydrocarbon radical, Hal represents a halogen, i.e., bromine, chlorine, flourine, or iodine, M is an alkali metal such as sodium or potassium, Me is methyl, and R is a divalent hydrocarbon radical, preferably a saturated aliphatic radical, save for equation (j-2) where R is preferably arylene or an alkyl substituted arylene radical;

The above equations also serve to illustrate the various types of divalent organic groups represented by R in formula (I). Preferably the divalent organic group is a -OC ,H group where a is an integer and the oxygen atom is linked directly to the silicon atom, or more preferably the divalent group is a divalent hydrocarbon group linked directly to the silicon atom as herein below defined.

The above equations represent processes well known in the art. Preferably siloxane block copolymers of this invention are prepared by the known platinumcatalyzed addition of a hydrosiloxane to an olefinically unsaturated ether or a polyether. Illustrations of ether intermediates for preparation of surfactants of the invention are vinyl, allyl and methallyl ethers, polyethers such as vinyl, allyl, methallyl terminated triglycols, diethylene glycols and polyethers having molecular weights of ISO to 900 based on the weight of the oxyalkylene groups and the like. Such intermediates are terminated or capped with a group represented by X in formula (I).

The siloxane block copolymers useful as surfactants in this invention contain one or more siloxane groups represented by formula (I) wherein b is 2 and both R groups are monovalent hydrocarbon groups wherein either the same hydrocarbon groups are attached to the silicon atoms (e.g. dimethylsiloxy, diphenylsiloxy, diethylsiloxy and the like) or different hydrocarbon groups are attached to the silicon atoms (e.g. methylphenylsiloxy, phenylethylsiloxy, and the like). The C- polymers also contain one or more siloxane groups represented by formula I wherein at least one R group is a R'(R"fiX radical as defined above. By way of illustration ethylenemethylsiloxy groups ethyleneoxymethylsiloxy groups and the like can be present in the copolymer. Thus the copolymers of this invention can contain trifunctional siloxane groups (e.g. monomethylsiloxane groups, CH SiO difunctions siloxane groups (e.g. dimethylsiloxane groups, (CH SiO), monofunctional siloxane groups, (e.g. trimethylsiloxane groups, (CH SiO), or combinations of these types of siloxane groups having the same or different substituents. Due to the functionality of the siloxane groups, the copolymer can be predominantly linear or cyclic or crosslinked or it can have combinations of these structures.

The siloxane portion of the block copolymers useful as surfactants in this invention can contain organic endblocking or chain terminating organic groups, in addition to the monofunctional siloxane chain terminating groups encompassed by formula l By way of illustration, the siloxane portion can contain such organic endblocking groups as hydroxyl, aryloxy groups (such as phenoxy), alkoxy groups (such as methoxy, ethoxy, propoxy and butoxy), acyloxy groups (such as acetoxy), and the like.

The siloxane portion of the block copolymers useful in this invention can contain, in addition to the groups represented by formula (I), minor amounts of siloxane groups represented by the formula:

e i-gel-fl wherein R has the meaning defined in formula (I), e has a value from 0 to 2,fhas a value from 1 to 2 and (e f) has a value from 1 to 3, inclusive.

The preferred siloxane block copolymers employed in this invention are those of formula (I) above wherein n is an integer, i.e., siloxane-oxyalkylene block copolymers. The oxyalkylene portions or blocks of these siloxane-oxyalkylene block copolymers are composed of oxyalkylene groups represented by the formula wherein R' is an alkylene group, with the proviso that at least 35 weight per cent, preferably 50 up to and including weight per cent of the oxyalkylene groups are oxyethylene groups. Illustrative of the oxyalkylene groups that are represented by formula (II) are oxyethylene, oxypropylene, oxy-l ,4-butylene, oxy-l ,5- amylene, oxy-2,2-dimethyl-l ,3-propylene, oxy-1,l0- decylene and the like. The oxyalkylene portion of the copolymers can contain more than one of the various types of oxyalkylene groups represented by formula (II), provided that at least 35 weight per cent of the oxyalkylene groups are oxyethylene groups. By way of illustration, the oxyalkylene blocks can contain only oxyethylene groups or both oxyethylene and oxypropylene groups, or other combinations of oxyethylene groups and the various other types of oxyalkylene groups represented by formula (II). Preferably the oxyalkylene groups consist of oxyethylene or a mixture of oxyethylene and oxypropylene radicals.

Accordingly the term block copolymer is used herein to denote a material wherein at least one section (block) of the molecule is composed of recurring monomeric units of one type and at least one other section (block) of the molecule composed of recurring monomeric units of a different type. The different sections or blocks in the molecule can be arranged in any configuration (e.g., AB, ABA, branched or cyclic). Thus the term block copolymers as used herein includes graft copolymers. The block copolymers used in this invention can be discrete chemical compounds. Usually, however, the block copolymers are mixtures of various discrete block copolymeric species. The block copolymers are usually mixtures due, at least in part, to the fact that the siloxane and polyoxyalkylene reactants used to produce the block copolymers are themselves usually mixtures.

Illustrative of the various organic terminal groups represented by X in formula (I) above are such endblocking groups as hydroxy; alkoxy (such as methoxy, ethoxy, propoxy, butoxy and the like); aryloxy (such as phenoxy and the like); arylkyloxy (such as benzyloxy, phenylethoxy and the like); alkenyloxy (such as vinyloxy, allyloxy and the like); acyloxy (such as acetoxy and the like); carbamyloxy (such as OOCNHCH -OOCNHC I-l and the like); and carbonate groups (such as OCOOCl-I and the like). Moreover in the siloxane-oxyalkylene block copolymers a single group can serve as an end-blocking group for more than one oxyalkylene chain. For example, the glyceroxy group,

can serve as an end-blocking group for three oxyalkylene groups. Trihydrocarbylsiloxy groups (e.g., trimethylsiloxy groups) can also endblock the oxyalkylene chains. Preferably X is a lower alkoxy radical.

Illustrative of the preferred divalent hydrocarbon groups represented by R in formula (I) are alkylene groups (such as methylene, ethylene, propylene, butylene, 2,2-dimethyl-l,3-propylene, decylene and the like); arylene groups such as phenylene, p,p'- diphenylene, and the like); and alkarylene groups (such as phenylethylene and the like). Preferably, the divalent hydrocarbon group is an alkylene group containing from two to four carbon atoms. Siloxane groups containing divalent hydrocarbon groups as substitutents are illustrated by groups having the formulae (3'13 -CH CH Si -CH CHCH Si0 p. and

Siloxane-oxyalkylene block copolymers that are especially suited for use as surfactants in this invention are those having the formula wherein Z has a value or 0 or 1; n has a value from 1 to inclusive, preferably 2 to 7 inclusive; y has a value from 1 to 10 inclusive, preferably 2 to 6 inclusive; a has a value from 2 to 4 inclusive; preferably 2 to 3 inclusive; x has a value from 2 to 4 inclusive; b has a value from 0 to inclusive, preferably 3 to 10 inclusive; R" is a hydrogen atom, an alkyl radical, an aryl radical, an aralkyl radical, an acyl radical, a carbamyl radical or a carbonate radical, more preferably an alkyl radical containing from one to four carbon atoms, especially methyl; and R is an alkyl radical, an aryl radical, or na aralkyl radical, preferably an alkyl radical containing from one to four carbon atoms, especially, methyl.

While the siloxane block copolymers of this invention can have molecular weights ranging from about 500 to about 4,000 and contain from about to about 90 weight per cent siloxane based on the weight of the copolymer, preferably they have molecular weights ranging from about 500 to about 2,500 and contain about 40 to 70 weight per cent siloxane. Conversely the --R (R") X substituents in formula (I) of the copolymers comprise from about 75 to about 10 weight per cent of the black copolymer and preferably from about 60 to about weight per cent.

The siloxane block copolymer surfactants employed as the foam stabilizers in this invention can vary over wide ranges and are generally employed in amounts ranging from about 0.025 to about 5 parts by weight or greater, per hundred parts by weight of the organic polyol starting material. Genrally there is no commensurate advantage to using amounts of surfactant greater than about 5 parts by weight, while the use of amounts below 0.025 parts by weight can detract from stability against foam shrinkage. Preferably the siloxane block copolymers are employed in amounts ranging from about 0.05 to about 1.5 parts by weight per hundred parts by weight of the organic polyol starting material.

The polyhydroxyl reactants (organic polyols) employed in this invention as the starting materials to prepare the polyurethane foams can be any polyether triol containing at least 40 mole per cent of primary hydroxyl groups and having a molecular weight from about 2,000 to about 8,000. Conversely said polyether triols can contain no more than 60 mole per cent of secondary hydroxyl groups. Preferably said polyether triols contain about 60 to mole per cent of primary hydroxyl groups and have a molecular weight from about 4,000 to about 7,000.

The preferred polyether triols of this invention are polyalkyleneether triols obtained by the chemical addition of alkylene oxides to trihydroxyl organic containing materials, such as glycerol; l,2,6-hexanetriol; 1,1 ,ltrimethylolethane; l,l,l-trimethylolpropane; 3-(2- hydroxyethyoxy )-l ,2-propanediol; 3 2- hydroxypropoxy)-l,2-propanediol; 2,4-dimethyl-2-(2- hydroxyethoxy)methylpentanediol-l ,5-; 1,1 l -tris [(2- hydroxyethoxy)methyl]ethane; 1,1 l -tris[ (2- hydroxypropoxy)methyl]-propane; and the like, as well as mixtures thereof.

Alternatively the organic polyol starting materials of this invention can be mixtures consisting essentially of said above defined polyether triols and other. polyether polyols having an average of at least two hydroxyl groups, said above defined polyether triols amounting (III) to at least 40 preferably at least 50, weight per cent of the total polyol content of the mixtures. Illustrative of such other polyethers are triols outside of the scope defined above, diols, tetraols and polymer/polyols, and the like, as well as mixtures thereof.

Examples of such polyether polyols that can be mixed with the above defined polyether triols include those adducts of alkylene oxide to such polyols as diethylene glycol; dipropylene glycol; pentaerythritol; sorbitol; sucrose; lactose; alpha-methylglucoside; alpha-hydroxyalkylglucoside; novolac resins; water; ethylene glycol; propylene glycol; trimethyl glycol; 1,2- butylene glycol; 1,3-butanediol; 1,4-butanediol; 1,5- pentanediol; 1,2-hexane glycol; 1,10-decanedio; 1,2-

cyclohexanediol; 2'butene-l ,4-diol; 3-cyclohexene- 1,1-dimethanol; 4-methyl-3-cyclohexene-l l dimethanol; B-methylene-l ,5pentanediol;

(2-hydroxyethoxy)- l -propanol; 4-(2-hydroxyethoxy l-butanol; 5-(2-hydroxypropoxy)-2-octanol; 3-allyloxyl ,S-pentanediol; 2-allyloxymethyI-Z-methyll, 3-propanediol; [4,4-pentyloxymethyl1-l 3- propanediol; 3-(o-propenyl-phenoxy) l ,2-propanediol; 2,2-diisopropylidenebis(p-phenyleneoxy)-diethanol; and the like, or phosphoric acid; benzenephosphoric acid; polyphosphoric acids such as tripolyphposphoric acid and tetrapolyphosphosoric acid; and the like; as well as mixture thereof.

Another type of polyether polyol that can be mixed with the above defined polyether triols and used as the starting materials of this invention are graft polymer/- polyether compositions obtained by polymerizing ethyleneically unsaturated monomers in a polyether as described in British Pat. No. 1,063,222 and U.S. Pat. No. 3,383,351, the disclosures of which are incorporated herein by reference thereto. Suitable monomers for producing such compositions include, for example, acrylonitrile, vinyl chloride, styrene, butadiene, vinylidine chloride, and thelike. Suitable polyethers for producing such compositions include, for example those polyethers hereinabove-described. These graft polymer/polyether compositions can contain from about 1 to about 70 weight per cent, preferably about 5 to about 50 weight per cent and most preferably about to about 40 weight per cent of the monomer polymerized in the polyether. Such compositions are conveniently prepared by polymerizing the monomers in the selected polyether at a temperature of 40 to 150C. in the presence of a free radical polymerization catalyst, such as peroxides, persulfates, percarbonates, perborates and azo compounds as more fully described by the above patent references. The resulting compositions may contain a small amount of unreacted polyether, monomer and free polymer as well as the graft polymer/polyether complex. Especially preferred are the graft polymer/polyethers obtained from acrylonitrile and polyether triols.

The alkylene oxides employed in producing the preferred polyethers described above normally have from two to four carbon atoms, inclusive while propylene oxide and mixtures of propylene oxide and ethylene oxide are especially preferred.

The exact organic polyol or polyols employed as the starting materials of this invention merely depend on the end use of the cold cure polyether urethane foam. For instance, the employment of polyether triols having at least 40 mole per cent primary hydroxyl groups and molecular weights from 2,000 to 8,000 preferably 4,000 to 7,000 generally have hydroxyl numbers from 84 to 21, preferably 42 to 28 and give primarily flexible polyether foams. The supplementary polyethers which may have any proportion of primary to secondary hydroxyl groups and which may be mixed with the required polyether triols can be used to control the degree of softness of the foam or vary the load bearing properties of the foam. Such limits are not intended to be restrictive, but are merely illustrative of the large number of possible combinations of polyether triols and other polyethers that can be employed.

The hydroxyl number is defined as the number of milligrams of potassium hydroxide required for the complete neutralization of the hydrolysis product of the fully acetylated derivative prepared from 1 gram of polyol or mixtures of polyols with or without other crosslinking additives used in the invention. The hydroxyl number can also be defined by the equation:

wherein OH hydroxyl number of the polyol.

A variety of organic isocyanates can be employed in the foam formulations of this invention for reaction with the organic polyol starting materials above described to provide cold cure polyether urethane foams. Preferred isocyanates are polyisocyanates and polyisothiocyanates of the general formula:

(QNCYli wherein Y is oxygen or sulfur, i is an integer of two or more and Q is an organic radical having the valence of i. For instance, Q can be a substituted or unsubstituted hydrocarbon radical, such as alkylene and arylene, having one or more aryl-NCY bonds and/or one or more alkyl NCY bonds. Q can also include radicals such as QZQ, where Q is an alkylene or arylene group and Z is a divalent moiety such as O, OQO, CO, CO S, SQS, SO and the like. Examples of such compounds include hexamethyl diisocyanate, 1,8diisocyanato-p-menthane, xylylene diisocyanate, (OCNCH CH CH OCHQ O, l-methyl- 2,4-diisocyanatocyclohexane, phenylene diisocyanates, tolylene diisocyanates, chlorophenylene diisocyanates, diphenylmethane-4,4'-diisocyanate, naphthalene-l ,5- diisocyanate, triphenylmethan e-4,4 -4 '-triisocyanate and isopropylbenzenealpha-4-diisocyanate.

Further included among the isocyanates useful in this invention are dimers and trimers of isocyanates and diisocyanates and polymeric diisocyanates such as those having the general formula:

in which i and j are integers of two or more, and/or (as additional components in the reaction mixtures) compounds of the general formula:

in which i is one or more and L is a monofunctional or polyfunctional atom or radical. Examples of this type include ethylphosphonic diisocyanate, C H P(O) (NCO) phenylphosphonic. diisocyanate, C H P(O) (NCO)2; compounds containing a Si-NCO group, isocyanates derived from sulfonamides (QSO NCO), cyanic acid, thiocyanic acid, and compounds contain ing a metal NCO radical such as tributyltinisocyanate.

More specifically, the polyisocyanate component employed in the polyurethane foams of this invention also include the following specific compounds as well as mixtures of two or more of them: 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, crude tolylene diisocyanate, bis(4-isocyanatophenyl)methane, polymethylene polyphenylisocyanates that are produced by phosgenation of anilineformaldehyde condensation products, dianisidine diisocyanate, toluidine diisocyanate, xylylene diisocyanate, bis(2-isocyanatoethyl)- fumarate, bis(2-isocyanatoethyl)carbonate, 1,6- hexamethylenediisoocyanate, l ,4-tetramethylenediisoocyanate, 1,10-decamethylene-diisocyanate, cumene-2,4-diisocyanate, 4-methoxy-l,3-phenylene diisocyanate, 4-chloro-l,3phenylenediisocyanate, 4- bromo-l ,3-phenylenediisocyanate, 4-ethoxy-l ,3- phenylenediisocyanate 2 ,4 -diisocyanatodiphenylether, 5 ,6-dimethyl-l ,3- phenylenediisocyanate, 2,4-dimethyl-l ,3- phenylenediisocyanate, 4,4-

diisocyanatodiphenylether, bis 5,6-(2-isocyanatoethyl)bicyclo [2.2.1]hep-2-ene, benzidinediisocyanate, 4,6-dimethyl-l ,3phenylenediisocyanate, 9,10- anthracenediisocyanate, 4,41 diisocyanatodibenzyl, 3,3-dimethyl-4,4diisocyanatodiphenylmethane, 2,6- dimethyl-4,4'-diisoocyanatodiphenyl, 2,4-

diisocyan atostilbene 3 ,3 '-dimethyl-4,4 diisocyanatodiphenyl, 3 ,3 '-dimethoxy-4,4 diisocyanatodiphenyl, 1,4-anthracenediisocyanate,

2,5-f1uorene-diisocyanate, l ,8- naphthalenediisocyanate, 2,6-diisocyanatobenzfuran, 2,4,6-toluenetriisocyanate, and many other organic polyisocyanates that are known in the art, such as those that are disclosed in an article by Sieflten, Ann., 565, (1949). In general, the aromatic polyisocyanates are preferred.

llll

Particularly useful isocyanate components of high resilience cold cure formulations within the scope of this invention are combinations of isomeric tolylene diisocyanates and polymeric isocyanates having units of the formula wherein R is hydrogoen and/or lower alkyl and x has a value of at least 2.1. Preferably the lower alkyl radical is methyl and x has a value of from 2.1 to about 3.0.

The amount of polyisocyanate employed will vary slightly depending on the nature of the polyurethane being prepared. In general the polyisocyanates are employed in the foam formulations of this invention in amounts that provide from 80 to 150 per cent, preferably from 90 to 1 per cent of the stoichiometric amount of the isocyanato groups required to react with all of the hydroxyl groups of the organic polyol starting materials and with any water present as a blowing agent. Most preferably, a slight amount of isocyanato groups in excess to the stoichiometric amount is em ployed.

The blowing agents employed in this invention include methylene chloride, water, liquefied gases which have boiling points below 80F. and above 60F., or by other inert gases such as nitrogen, carbon dioxide, methane, helium and argon. Suitable liquefied gases include saturated aliphatic fluorohydrocarbons which vaporize at or below the temperature of the foaming mass. Such gases are at least partially fluorinated and can also be otherwise halogenated. Fluorocarbon blowing agents suitable for use in foaming the formulations of this invention include trichloromonofluoromethane, dichlorodifluoromethane, dichlorofluoromethane, 1,1- chloro-l-fluoroethane, l-chloro-l,l-difluoro, 2,2- dichloroethane, and l,l,l-trifluoro, 2-chloro-2-fluoro, 3,3-difluoro-4,4,4-trifluorobutane. The amount of blowing agent used will vary with density desired in the foamed product. Usually from 2 to parts by weight of the blowing agent per 100 parts by weight of the organic polyol starting materials are preferred.

The catalysts employed in this invention include any of the catalyst used in producing conventional flexible polyurethane foam. Because of the high degree of reactivity of the cold cure, high resilience polyether urethane foam system of this invention amines rather than metal/amine combinations are preferred. Illustrative of such conventional amine catalyst are N-methyl morpholine, N-ethyl morpholine, hexadecyl dimethylamine, triethylamine, N,N,N ',N -tetramethyl-l ,3- butanediamine, N,N-dimethylethanolamine, bis(2- dimethylaminoethyl)ether, N,N,N'N'-tetramethyl ethylenediamine, 4,4'-methylene bis(2-chloroaniline), dimethyl benzylamine, N-cocomorpholine, triethylene diamine, [l,4-diazobicyclo(2,2,2)-octane], the formatc salts of triethylene diamine, other salts of triethylene diamine and oxyalkylene adducts of primary and secondary amino groups, and the like. Such amine catalysts are preferably employed in the mixtures in an amount from 0.1 to 0.5 or 2 weight per cent based on the total weight of the organic polyol starting materials. However, if desired, conventional metal catalysts may be used to supplement the preferred amine catalysts. Illustrative of such metal catalysts are the tin salts of various carboxylic acids and nickel acetylacetonates.

The relative amounts of the various components reacted in accordance with the above described process for producing cold cure polyether urethane foams in accordance with this invention are not narrowly criti cal. The polyether and the polyisocyanate are present in the foam formulations used to produce such foams in a major amount. The relative amounts of these two components is the amount required to produce the urethane structure of the foam and such relative amounts are well known in the art. The blowing agent, catalyst and surfactants are each present in a minor amount necessary to achieve the function of the component. Thus, the blowing agent is present in a minor amount sufficient to foam the reaction mixture, the catalyst is present in a catalytic amount (i.e., an amount sufficient to catalyze the reaction to produce the urethane at a reasonable rate) and the surfactants are present in a foam-stabilizing amount (i.e., in an amount sufficient to stabilize the foam against voids and shrinkage). Pre ferred amounts of these various comments are given hereinabove.

The cold cure urethane foams produced in accordance with this invention can be used for the same purposes as corresponding conventional hot cure polyether urethane foams, e.g. they can be used wherever cushioning is desired, e.g. in furniture; in transportation systems, automobiles, planes, etc.; in carpeting; in the packaging of delicate objects; and the like.

Other additional ingredients can be employed in minor amounts in producing the cold cure polyether urethane foams in accordance with the process of this invention, if desired, for specific purposes. Thus inhibitors (e.g. d-tartaric acid and tertiary-butyl pyrocatechol, Ionol) can be employed to reduce any tendency of the foam to hydrolytic or oxidative instability. Flame retardants (e.g. tris(2-chloroethyl)phosphate can be used. Dihydrocarbon silicone oils, e.g. dimethylsiloxanes, have been successfully mixed with the siloxane block copolymers employed in this invention to provide cold cure polyether urethane foams with fine cell structure with little or no shrinkage. Such mixtures help expand the usefulness of the siloxane block copolymers by broadening the copolymer concentration range, providing more processing latituted and increasing the adaptability of the block copolymer to a variety of foam formulations. Of course any suitable organic solvent for the amine catalyst and/or for the siloxane block copolymers can be used which does not substantially adversely effect the oepration of the process or reactants. Examples of such solvents for the catalysts include, e.g., polyols, such as hexylene glycol (i.e. 2-methyl-2,4-pentanediol), dipropylene glycol, and the like. Examples of such solvents for the block copolymers include e.g. hydrocarbons; halohydrocarbons; organic polyether compounds such as the adducts of alkylene oxide and monols, diols or triols, such as C H O(C H O), (C I-I O), I-I, and dipropylene glycol; alkyl phthalates, such as dioctyl phthalate; and the like. Such siloxane block copolymer-solvent solutions preferably contain from 25 to parts by weight of the copolymer per parts by weight of the solvent and the copolymer but can contain from I to 99 parts by weight block copolymers are polyether triols such as adducts of ethylene oxide, propylene oxide or mixtures thereof with triol starters such as glycerol, 1,2,6 hexanetriol and the like. Examples of other additives that can be employed are crosslinkers such as glycerol, triethanol amine and their oxyalkylene adducts and anti- 1O yellowing agents. Still other additives include organic surfactants such as nonionic, anionic, cationic and amphoteric surfactants, (e.g. C H, C I-I.,(OC H -OH). Such organic surfactant additives are especially useful when aqueous solutions of the siloxane block copolymer are employed for they serve to raise the cloud point of said aqueous solutions and to protect them from adversely high ambient temperatures which may be encountered during storage and shipping.

In accordance with this invention, the cold cure polyether urethane foams can be produced by any suitable technique. The preferred process is a one-step or one shot technique wherein all of the reactants are reacted simultaneously with the foaming operation. A second general process is called the prepolymer process whereby a prepolymer is formed by reacting the polyether starting material with a small excess of the isocyanate and later foaming the prepolymer by the reaction with water or an inert blowing agent. Another method which can be used is the quasi-prepolymer technique which involves reacting a large excess of the isocycnate with the polyether starting material and then subsequently foaming this product with additional polyether in the presence of a blowing agent. Sometimes it is preferred to premix the polyether starting material and siloxane block copolymer although any suitable premixture of the various ingredients can be used. Because of the high exothermic nature of the reaction cold cure urethane foams are rapidly produced without the need of any external heat by mixing the reactants at ambient temperatures and pouring the foaming reaction mixture into a suitable mold and allowing the foam to cure itself. Of course, if desired the overall reaction can be even further accelerated by preheating the mold and or employing conventional high temperature post curing procedures. Within a shorter period of time the cold cure process, with or without post cure, simultaneously achieves a greater degree of cure throughout the entire foam, and shorter tack free and demolding time, then is generally achieved with conventional hot cure processes. For instance, cold cure foams can be removed from the mold far sooner without substantial damage to the surface than conventional hot cure foams. Of course it is to be understood that the cold cure foams of this invention can also be prepared in stabstock form, if desired.

An additional feature of the instant invention are the novel compositions suitable for use in producing cold cure polyether foam.

Such compositions include for example, those comprising (I) an organic polyol, (II) a polyisocyanate, said organic polyol and polyisocyanate being present in the composition in a major amount, (III) a minor amount.

of a blowing agent, (IV) a minor amount of an amine catalyst and (V) a minor amount of a siloxane block copolymer, said ingredients being those herein defined. The preferred compositions are those containing the preferred ingredients in their preferred amounts, both of which are also defined herein. Of course it is to be understood that the ingredients of the above compositions can be mixed and added in any suitable manner prior to commencing the cold cure reaction. Illustrative examples of preferred premixes include premixes of the organic polyol and siloxane block copolymer, which may also optionally contain an amine catalyst, and aqueous premixes of the siloxane block copolymer, amine catalyst, and an organic surfactant to raise the cloud point of said aqueous premixes.

The following examples illustrate the present invention and are not to be regarded as limitative. It is to be understood that Me represents a methyl radical, Et represents an ethyl radical, p.h.p. refers to parts of active siloxane block copolymer per hundred parts of organic polyol starting material and that all of the parts, percentages and proportions referred to herein and in the appended claims are by weight unless otherwise indicated.

For the sake of brevity the following designations are used to denote the various ingredients employed in the examples.

TABLE I Compositions of siloxane block copolymers having the generic formula Me SiO(Me SiO),[RO(C=;H O),,,(C I-[ 0),.C,,H ,,SiMeO] SiMe,

Wt. mol. percent Ethylene IIBiloxane X y m n R a wt. Siloxane Oxide I 2.0 2.8 0 3 Me 2 1,000 47 100 III 4.0 2.8 0 3 Me 2 1,160 54 100 III 12.9 1.5 0 3 Me 2 750 62 100 IV 2.8 1.9 0 0 Et 3 643 75 0 V 7.0 3.0 0 3 Me 2 1,430 0 V1 7.0 3.0 2.5 3.3 Me 3 1,910 45 50 V11 7.0 3.0 6.0 7.9 Me 3 3,100 28 50 VIII 0 1.0 O 7.0 Me 3 570 39 100 IX 72 5 .0 29 20 Me 3 19,000 31 35 X 3.2 29 20 Me 3 14,000 41 35 XI 0 3.0 0 7.0 Me 3 1,390 25 K11 72 5.0 2.5 3. Me 3 7,500 77 100 "Adduct of SiH with allylether ltiiloxanes l to VII represent block copolymers useful in this invention. .iailoxanes Vlll to XIII represent block eoplymers not useful in this invention.

TABLE I1 EMPERICIAL FORMULA FOR COPOLYMERS USEFUL FOR STABILIZATION OF COLD CURE FLEXIBLE POLYETHER URETHANE FOAM Organic Polyols El This is a polyether triol,

mol. wt. about 5,000; hydroxyl No about 34; containing about 75 mole primary hydroxyl groups produced by reacting about 84% propylene oxide and about 16% ethylene oxide with glycerol. This is a graft polymer/ polyol; about wt.% graft polymer and about 80 wt. polyol; hydroxyl No. about 28, produced by polymerizing acrylonitrile in El. This is a mixture of polyether triols, about 97.6 wt. El and about 2.4 wt. of a polyether triol, mol. wt. about 270; hydroxyl No. about 625, containing about 75 mole primary hydroxyl groups produced by reacting ethylene oxide with glycerol. This is a polyether triol, mol. wt. about 270; hydroxyl No. about 625 containing about 75 mole primary hydroxyl groups produced by reacting ethylene oxide with glycerol. This is a polyether diol, mol. wt. about 2,300 hydroxyl No. about 49, containing about 45 mole primary hydroxyl groups produced by reacting about 93% propylene oxide and about 7% ethylene oxide with dipropylene glycol. This is polyether triol, mole. wt. about 270, containing about 19 mole primary hydroxyl groups produced by reacting propylene oxide with glycerol. This is a mixture of about 86.5 wt. E4 and about 13.5 wt. ethylene glycol, having a hydroxyl No. of about 775-795 and containing about 70-80 mole percent primary hydroxyl groups.

Polyisocyanate Catalysts Cl This is a mixture of about 80 wt. 2,4- tolylene diisocyanatc and about 20 wt. 2,6-tolylene diisocyanate.

TABLE III-Continued Designation Composition C2 This is the isocyanate polymeric residue having an amine equivalent No.

of about 106 of the production of Cl.

This is a polymethylene polyphenyl isocyanatc polymer containing about 2.6-2.9 moles of NCO per mole of polymer and having an isocyanatc content of about 3 l .4 percent.

This is a corn osition of about 60 wt. 0 C3 and about 40 wt. Cl.

This is a composition of about 84 wt. Cl and about 16 wt. E6.

This is a composition of about 50 wt. C5 and about 50 wt. C3.

This is a composition consisting of about 64 wt. C5; about 21.5

wt. Cl and about l4.5 wt. of tris(2'chloroethyl)phosphate.

This is a composition consisting of about 50 vcvtz. Cl and 50 wt.

Amine Catalysts EXAMPLE 1 This example demonstrates the superiority of the siloxane block copolymers of this invention over similar siloxane block copolymers but outside of the scope of this invention in producing high resilient cold cure polyether urethane foams of improved cell structure without substantial foam shrinkage.

The foam formulations employed in producing the foams in this example were identical save for variations in the amount and siloxane block copolymer employed. The high resilient cold cure polyether foams were prepared by adding the ingredients to a mold and allowing the formulations to cure at ambient temperature. Thereafter the foam containing moles were placed in an oven at C. for about 2 minutes to facilitate separation of the paper liner from the cardboard mold. Said formulations contained lOO parts by weight of organic polyols on the order of about 60 parts of polyether triol E3, about 30 parts of graft polymer/triol E2 and about 10 parts of polyether diol E5; about 2.5 parts by weight of water; about 0.1 part by weight of amine catalyst A1; about 1.0 parts by weight of amine catalyst A2; about 5 parts by weight of trichlorofluoromethane and about 37.5 parts by weight of polyisocyanate C6. The amount of nature of the siloxane block copolymer used was varied as reported in the following table which also reports on the cell structure and the shrinkage of the uncrushed cold cure polyether urethane foams produced.

TABLE IV llliloxane Cells Foam lBiloxane Block Concentration Per No. Eopolymer lphp.) Inch Shrinkage ll None (Control) 22 None Copolymers of this invention 2 l5iloxane I 0.05 126 None 3 lzliloxane I 0.25 30 None 4 IBiloxane I 0.5 34 None 5 lfiiloxane III 0.025 26 None 6 liiloxane III 0.05 30 None I lliiiloxane Ill 0.25 42 Slight B lliiiloxane IV 0.025 130 None 9 lililoxane IV 0.05 40 Slight I lBiloxane V 0.025 30 None ll 1 Siloxane V 0.05 36 Slight l2 lililoxarle VI 0.05 28 Slight l3 liloxane VII 0.05 126 None Copolymers not of this invention 14 lIEiloxane Vlll 0.5 124 Slight l5 lEiloxane X 0.025 24 Moderate 16 lziiloxane XI 0.5 22 None l7 l5iloxane XII 0.05 8 Moderate 18 liiloxane XIII 0.05 26 Moderate EXAMPLE 2 cold cure polyether urethane foams having improved This example demonstrates the improvement in cell structure with little if any shrinkage of the cold cure polyether urethane foams by employing the siloxane block copolymers of this invention. The foams were produced in the same manner as Example 1, using formulations containing 100 parts by weight of organic polyol composition consisting of 98.0 parts by wt. of a blend of about 80 wt. polyether triol El and about 20 wt. graft polymer/triol E2 and about 2.0 parts by weight of triethanolamine; about 2.8 parts by weight of water, about 1.0 parts by weight of amine catalyst A2; about 0.3 parts by weight of triethylamine catalyst, and about 41.2 parts by weight of polyisocyanate C4. Again the amount and nature of the siloxane block copolymer used was varied as reported in the following table which also reports on the cell structure and the shrinkage of the uncrushed cold cure polyether urethane cell structure with little if any shrinkage. The foams were produced in the same manner as Example 1, using formulations containing 100 parts by weight of polyether triol El about 7.0 parts by weight of triethanolamine, about 3.2 parts by weight of water, about 1.5 parts by weight of amine catalyst A2, about 5.0 parts by weight of tris(2-chloroethyl)phosphate a flame retardant, and about 53.1 parts by weight of polyisocyanate C8. Again the amount and nature of the siloxane block copolymer used was varied as reported in the following table which also reports on the cell structure and the shrinkage of the uncrushed cold cure polyether urethane foams. The foams were also subsequently crushed and given a resilience test according to ASTM D-l564-R. The resilience test is also referred to as the Nopco Per cent Ball Rebound test and is reported in the Handbook of Foamed Plastics by R. .I. Bender,

foams produced. p. 66 (1965). These values for said foams are also re- TABLE V Siloxane Cells Foam Siloxane Block concentration Per Cell op lyme {p.hp.) Inch Shrinkage Uniformity 1 None (Control) 25 None Voids Copolymers of this Invention 2 Siloxane III 0.05 36 None No Voids 3 S loxane III 0.10 40 None No Voids 4 S loxane [11 0.25 Moderate No Voids S S loxane 0.25 38 None No Voids 6 Siloxane I 0.50 40 None No Voids Copolymers not of this invention 7 Siloxane IX 0.05 30 Severe No Voids EXAMPLE 3 ported in the following table; a value of 45% or higher This example demonstrates that the siloxane block copolymers of this invention help provide high resilient indicates a high resilience for the foam. All the foams containing a siloxane block copolymer had approximately the same density and porosity.

TABLE VI Siloxane Cells Foam Siloxane Block Concentration Per Per Cent No. Copolymer (p.h.p.) Shrinkage Inch Ball Rebound 1 None (Control) None 26 57 Copolymers of this Invention 2 Siloxane I 0.25 None 36 54 3 Siloxane III 0. I0 None 40 54 Copolymers not of this invention 4 Siloxane XIII 0.10 Moderate 36 56 119 20 EXAMPLE 4 TABLE VIII-Continued This example demonstrates the improvement in cell F B in Extent oam ulstructure with little if any shrinkage of the cold cure No. Snoxane Block copolymer in |ches polyether urethane foams by employing a solvent solu- 5 4 Silomne Xm 285 non of the siloxane block copolymers of th1s invention. The foams were produced in the same manner as Example l, using formulations containing 100 parts by weight of polyether triol E1, about 7.0 parts by weight EXAMPLE 6 of triethanolamine, about 3.2 parts by weight of water, This example illustrates the improvement against about 1.5 parts by weight of amine catalyst A2, and flammability, in cell structure, and absence of shrinkabout 53.1 parts by weight of polyisocyanate C8. The age, provided by the siloxane block copolymers of this amount of the siloxane block copolymer used was varinvention in producing cold cure polyether urethane ied as reported in the following table, which also refoams which do not contain a flame retardant. The ports on the cell structure and the shrinkage of the un- 15 foams were produced in the same manner as Example crushed cold cure polyether urethane foams. 1, using formulations containing 100 parts by weight of TABLE Vll Siloxane Cells Foam Siloxane Block Concentration Per Quality No. Copolymer (p.h.p.) lnch Shrinkage of Foam 1 None (Control) 22 None Bottom and Side Voids 2 Siloxane ll 0.19 35 None No Voids 3 Siloxane ll 0.12 35 None No Voids Used as a 15/85 wt. solutionn of Siloxane 11 in C H O(C H O) (C H,;O), H. Used as a 10/90 wt. 72 solution of Siloxane 11 in C H O(C, .H O)\(C, H

EXAMPLE 5 organic polyol on the order of about 85 parts of polyether triol E3 and about 15 parts of polyether triol E7; This example demonstrates that the siloxane block about 2.5 parts by weight of water; about 1.0 parts by copolymers of this invention cause little, if any, inweight of amine catalyst A2 and about 60.4 parts by crease in flammability of a flame retarded cold cure weight of polyisocyanate C7. The amount and nature foam, while a siloxane block copolymer not of this inof the siloxane block copolymer used was varied as revention aggravates burning. The foams employed were ported in the following table which also reports on the those of Example 3 and the extent of burning in inches cell structure, shrinkage and flammability of the unof the uncrushed foams was measured according to crushed cold cure polyether urethane foams produced. ASTM l692-67T and is reported in the following Ta- The flammability test was carried out according to ble. ASTM 169267T.

TABLE 1X Siloxane Burning Siloxane Block Concentration Cell Extent in Foam No. Copolymer (p.h.p.) Structure Shrinkage Inches 1 None (Control) Coarse None 0.99 Copolymer of this invention 2 Siloxane 1* 015 Fine None 0.89 Copolymer not of this invention 3 Siloxane lX** 0.08 Fine Severe 5.0

Used as a 20/80 wt. 7: solution of Siloxane I in C H O(C H Ol lc l'l ohsll "Used as a /45 wt. 70 solution of Siloxane [X in a 90/10 wt. "/a solvent mixture of C,H,,O(C H O),,,(C;,H O)|.'.H and a polyether adduct produced by reacting 10.5 moles of ethylene oxide and 1 mole of nonylphenol.

TABLE VIII EXAMPLE 7 This example lllustrates the use of combinations of siloxane block copolymers of this invention and dihysiloxane Block copolymer z fi fig drocarbon siloxane oils can be employed to provide umform fine-celled cold cure polyether urethane foams l Non m 1.92 with little, if any, shrinkage. The foams were produced W in the same manner as Example 1 while the foam forg lg: mulations were also the same as in Example 1 using Si- Copolymer not ofthis invention loxane 111, except that a dimethyl siloxane oil having the formula Me SiO(Me SiO) SiMe where Me is methyl and a viscosity of about 2 centistokes at 25C. was also employed. The amounts of Siloxane III and dimethyl siloxane oil were varied as reported in the following table along with the cell structure and shrinkage of the uncrushed cold cure polyether urethane foams produced.

filtrate was a siloxane block copolymer having the following average formula 5 The siloxane copolymer had a viscosity of about 13 centistokes at C.

This siloxane block copolymer was evaluated in the TABLE X Siloxane Block IDimethyl Copolymer Siloxane Oil Cells Foam Concentration Concentration Per Cell No. {p.lLp.) Lp.h.p.) Inch Shrinkage Structure 1 None (Control) None 22 None irregular 2 0.25 l .0 None uniform 3 0.50 112.0 30 None uniform 4 0. 17 0.33 37 None uniform EXAMPLE 8 production of cold cure polyether urethane foams. The

Cold cure foams were produced in the same manner as Example 2 while the foam formulations were also the same as in Example 2 using Siloxane III, except that a cyclic dimethyl siloxane oil consisting essentially of dimethyl tetramer was also employed. The amounts of Siloxane III and cyclic dimethyl oil were varied as reported in the following table along with the cell structure and shrinkage of the uncrushed cold cure polyether urethane foams produced.

20 foams were produced in the same manner as Example 1, using formulations containing 100 parts by weight of polyether triol E1, about 7.0 parts by weight of triethanol amine, about 3.2 parts by weight of water, about 1.5 parts by weight of amine catalyst A2, about 5.0

25 parts by weight of tris(2-chloroethyl)phosphate, and about 53.1 parts by weight of polyisocyanate C8. The amount of the siloxane block copolymer,

TABLE XI ISiloxane Block IDimethyl Copolymer Siloxane Oil Cells Foam Concentration Concentration Per Cell No. lp.h.p.) llj p.h.p.) Inch Shrinkage Structure 1 None (Control) None 25 None voids 2 0.1 None 40 None no voids 3 0.25 l.0 42 None no voids EXAMPLE 9 employed varied as reported in the following table A mixture of about 72.9 grams (0.43 mole of OEt) of equilibrated ethoxy-endblocked siloxanes, obtained by potassium silanolate catalyzed equilibration of cyclic dimethylsiloxanes, methyltriethoxysilane and dimethyldiethoxysilane, having the average structure.

about 77.1 grams (0.47 mole of OH) of dry methoxytriglycol, about grams of toluene, about 0.12 grams of anhydrous potassium acetate and 0.3 grams of trifluoroacetic acid was heated to reflux and the ethanol removed by azeotropic distillation through a packed column. About 3 grams of sodium bicarbonate was then which also reports on the cell structure and uniformity of the uncrushed foam produced.

The following premix solutions were prepared:

"Not of this invention.

"Without the organic nonionic surfactant. Siloxane II was insoluble in just the water plus amines of Solution A.

added and the solvent removed by sparging with nitrogen at l30C. and the stripped material filtered. The

Cold Cure Polyether urethane foams were prepared using the following formulations:

TABLE XIV Fl F2 F3* F4* Component Parts by Wt. Parts by Wt. Parts by Wt. Parts by Wt.

Polyol El 80.0 80.0 80.0 80.0 Polyol E2** 20.0 20.0 20.0 20.0 Solution A 4.3

Solution 1.0 Solution C 4.1 Water 2.7 N-athyl morpholine 0.2 0.2 triethylenediamine 1.0 1.0 Polyisocyanate*** 37.7 37.7 37.7 37.7

Not of this invention. "The polyols were employed as a blended premix with each other.

*The polyisocyanate was a blend of 40 wt. 7c Cl. 40 wt. 7r C2 and 20 wt. 71 C3.

Using charges based on 200 grams of organic polyol the above formulations were poured into an 8 inch by 8 inch by 6 inch cardboard box and allowed to react and cure at room temperature. The properties of the cation and the spirit and scope of the appended claims.

What is claimed is: 1. A composition suitable for use in producing a cold cure high resilience polyether urethane foam selected uncrushed cold cure polyether urethane forms ob 20 m h ClaSS Consisting of tained are shown in the following Table.

The following formulations were used to produce cold cure semi-flexible polyether urethane foam in the same manner as Example 1. The formulations con- 35 tained 100 parts by weight of organic polyol on the order of about 85 parts of polyether triol E3 and about parts of polyether triol E7; about 1.9 parts by weight I. a composition consisting essentially of a major amount of an organic polyol selected from the group consisting of (A) a polyether triol containing at least 40 mole per cent primary hydroxyl groups and having a molecular weight fromabout 2,000 to about 8,000 and (B) a mixture of said polyether triol and another polyether having an average of at least two hydroxyl groups, said polyether trio] of said mixture amounting to at least 40 weight per cent of the total polyol content, and a minor amount of a siloxane block copolymer having a molecular weight from about 500 to about 2,500, a siloxane content from about 40 to about 70 weight per cent based on the weight of the copolymer and an oxyethylene content of at least 35 per cent based on the total amount of any oxyalkylene groups present in said copolymer, said copolymer having the formula of water; about 1.3 parts by weight of amine catalyst A2; about parts by weight of calcium carbonate; about 1.0 parts by weight of carbon black and about 67.3 parts by weight of polyisocyanate C5. The amount and nature of the siloxane block copolymer was varied as reported in the following Table along with the properties of the uncrushed cold cure polyether urethane foams produced.

wherein 2: has a value of 0 or 1, n has a value from 2 to 7 inclusive, y has a value from 1 to 6 inclusive, 0 has a value from 2 to 4 inclusive, x has a value from 2 to 4 inclusive, b has a value of from 0 to 10 inclusive, R" is a member selected from the class of an alkyl radical, an aryl radical, an aralkyl radical, an acyl radical, a carbamyl radical and a carbonate radical and R is a monovalent hydrocarbon radical, and

TABLE XVI Siloxane Cells Siloxane Block Concentration per Cell Foam Foam No. Copolymer (p.h.p.) lnch Uniformity Shrinkage l None (Control) to Poor Copolymer of this Invention 2 Siloxane l 0.5 35 to 40 Good None 3 Siloxane l 1.0 40 Good Slight Copolymer not of this lnvention 4. Siloxane TX 0.25 Good Severe 5. Siloxane l)( 0.05 Good Severe Various modifications and variations of this invention will be obvious to a worker skilled in the art and it is to be understood that such modifications and variations are to be included within the purview of this appli- II. a composition consisting essentially of a major amount of water, a minor amount of an amine catalyst, a minor amount of an organic surfactant, and a minor amount of a siloxane block copolymer having a molecular weight from about 500 to about 2,500, a siloxane content from about 40 to about 70 weight per cent based on the weight of the copolymer and an oxyethylene content of at least 35 weight per cent based on the total amount of any oxyalkylene groups present in said copolymer, said copolymer having the formula minor amount of an amine catalyst is also present.

6. A composition as defined in claim 1 wherein the composition consists essentially of a major amount of water, a minor amount of an amine catalyst, a minor amount of an organic surfactant and a minor amount of the siloxane block copolymer.

7. A composition as defined in claim 6 wherein R is R" are methyl radicals, Z is l, y is 2 to 6 inclusive, a is 2 to 3 inclusive, and b is 3 to 10 inclusive.

5. A composition as defined in claim 2 wherein a wherein 2 has a value of or i, n has a value of from 2 to 7 inclusive, y has a value from 1 to 6 inclusive, a has a value from 2 to 4 inclusive, b has a value of from 0 to 10 inclusive, R" is a member selected from the class of an alkyl radical, an aryl radical, an aralkyl radical, an acyl radical, a carbamyl radical and a carbonate radical and R is a monovalent hydrocarbon radical.

2. A composition as defined in claim 1 wherein the composition consists essentially of a major amount of the organic polyol and a minor amount of the siloxane block copolymer.

3. A composition as defined in claim 2 wherein R is a methyl radical.

4. A composition as defined in claim 2 wherein R and a methyl radical.

8. A composition as defined in claim 6 wherein R and 10. A composition as defined in claim 6 wherein the siloxane block copolymer has the formula 11. A composition as defined in claim 6 wherein the siloxane block copolymer has the formula Page 1 Patent No. Date Inventor) E. L. Morehouse It is certified that error appears in the above-identified patent and that said Letters Patent are hereby corrected as shown below:

Column 1, line 5, "26" should be ---20--.

Column 1, line 34, "may" should be --many--.

Column 1, line 35, "manufacture" should be manufacturer--.

Column 1, line 62, "are" should be ---as--.

Column 1, last line, "form" should be -foam--.

. Column 2, line 1, "resistance" should be --resistance---.

Column 2, line 5, after "much" insert ---more---.

Column 2, line 35, "deform" should be ---deformed-.-

Column 3 line 42, "polymers" should be ---copolymers Column 3 line 57, "which" should be wh r In equation formula (k)" bridging columns 3 and delete the triple bonds after "ClCOCH and "HCl".

In equation formula "(m-l)" bridging columns 3 and 4 delete the triple bond "5" after "CH =CHCH OH".

Column 5, line 39, "difunctions" should be difunctional---.

(continued on page 2) UNITED STATES PATENT OFFICE IFICATE OF CORRECTION Page 2 Patent No. 3 887 ,483 Dated un 3 1975 Inventor(s) Morehouse It is certified that error appears in the above-identified patent a and that said Letters Patent are hereby corrected as. shown below:

Column 7, line 27 the right hand end of formula "III" shown as "SiR" should be ---SiR Column 7, line 32, "or" first occurrence should be Column 7 line 42, "na" should be ---an---.

Column 7 line 54, "black" should be -block--.

Column 8 line 45, "decanedio" should be --decanediol---.

Column 8 line 56, "tripolyphposphoric" should be ---tripolyphosphoric--.

Column 8, line 57, "tetrapolyphosphosoric" should be --tetrapolyphosphoric.

Column 8 line 58, "mixture" should be ---mixtures--- Column 10, line 55, "4,4'1" should be ---4,4'---.

Column 12, line 55, "oepration" should be operation--.

Column 13, line 31, "isocyenate" should be ---isocyanate--.

Column 14, line 9, "stabstock" should be --slabstock---.

Column 19 first footnote of "TABLE VII" "solution "should be ---solution---.

Continued on page 3 UNITED STATES PATENT OFFICE QERTEFECATE 0F CGRRECHQN P 3 Patent No. 3,887,483 n June 3, 1975 I t 0. Inventor) E. L. Morehouse It is certified that error appears in the above-identified patentand that said Letters Patent are hereby corrected as shown below:

Column 23, the fourth "Component" of "TABLE XIV" shown as "Solution" should be --Solut.i.on B-.

Colunm. 23, the seventh "Component" of "TABLE XIV'" shown. as "N-athyl morpholine" should be Nethyl morpholine---.

- Column 25 lines 13-29 delete said lines 13-29 and insert:

"-- \vltc rciit i list; a 'aluc. 01' u or l n" nzis ai'ntu'c' of now 2 to 7 inclusive, has a value from l to (1 inclusive, 0, has a value from 2 to 4 inclusive, b has a \lilllC of from '-O to 10 inclusive, R" is u mmhcr selected from the class often zallcyl radical, 2m :nyl radical, an :uzil'uyl redh; cal, an '.C)'l lzulicnl, a CtZIliItti-Qfl radical zmd :t ozuhonntq radical and it is Tt-lllOllUY-tltl'll hydrocarbon radical 2. A con t 'bsition as defines, in claim \s'hcrrcin the (imposition consists essentially of a IflfljOl' zm'tount of hc organic pol ol and a minor amount of the stloxanc alocl; copolymcr.

3. A composition as dcfim-d in claim 2 wherein R is a methyl radical. x

4. A composition as defined ih clzunt 2 wherein l\ and nivtlis'l uidihals, l. is t w 6 mclugvc a Signed and Sealed this twent -ei ht [SEAL] y 3 y f October 1975 RUTH C. MASON Atresting Officer C. MARSHALL DANN Commissioner rr/Pare'ntx and Trademarks 

1. A COMPOSITION SUITABLE FOR USE IN PRODUCING A COLD CURE HIGH RESILIENCE POLYETHER URETHANE FOAM SELECTED FROM THE CLASS CONSISTING OF
 1. A composition suitable for use in producing a cold cure high resilience polyether urethane foam selected from the class consisting of I. a composition consisting essentially of a major amount of an organic polyol selected from the group consisting of (A) a polyether triol containing at least 40 mole per cent primary hydroxyl groups and having a molecular weight from about 2,000 to about 8,000 and (B) a mixture of said polyether triol and another polyether having an average of at least two hydroxyl groups, said polyether triol of said mixture amounting to at least 40 weight per cent of the total polyol content, and a minor amount of a siloxane block copolymer having a molecular weight from about 500 to about 2,500, a siloxane content from about 40 to about 70 weight per cent based on the weight of the copolymer and an oxyethylene content of at least 35 per cent based on the total amount of any oxyalkylene groups present in said copolymer, said copolymer having the formula
 1. A COMPOSITION CONSISTING ESSENTIALLY OF A MAJOR AMOUNT OF AN ORGANIC POLYOL SELECTED FROM THE GROUP CONSISTING OF (A) A PO;YETHER TRIOL CONTAINING AT LEAST 40 MOLE PER CENT PRIMARY HYDROXYL GROUPS AND HAVING A MOLECULAR WEIGHT FROM ABOUT 2,000 TO ABOUT 8,000 AND (B) A MIXTURE OF AVERAGE OF AT LEAST TWO HYDROXYL GROUPS, SAID POLYETHER AVERAGE OF AT LEAST TWO HYDROXYL GROUPS, SAID POLYETHER TRIOL OF SAID MIXTURE AMOUNTING TO AT LEAST 40 WEIGHT PER CENT OF THE TOTAL POLYOL CONTENT, AND A MINOR AMOUNT OF A SILOXANE BLOCK COPOLYMER HAVING A MOLECUALR WEIGHT FROM ABOUT 500 TO ABOUT 2,500, A SILOXANE CONTENT OF AT LEAST ABOUT 40 TO ABOUT 70 WEIGHT PER CENT BASED ON THE WEIGHT OF THE COPOLYMER AND AN OXYETHYLENE CONTENT OF AT LEAST 35 PER CENT BASED ON THE TOTAL AMOUNT OF ANY OXYALKYLENE GROUPS PRESENT IN SAID COPOLYMER, SAID COPOLYMER HAVING THE FORMULA
 2. A composition as defined in claim 1 wherein the composition consists essentially of a major amount of the organic polyol and a minor amount of the siloxane block copolymer.
 3. A composition as defined in claim 2 wherein R is a methyl radical.
 4. A composition as defined in claim 2 wherein R and R'''' are methyl radicals, Z is 1, y is 2 to 6 inclusive, a is 2 to 3 inclusive, and b is 3 to 10 inclusive.
 5. A composition as defined in claim 2 wherein a minor amount of an amine catalyst is also present.
 6. A composition as defined in claim 1 wherein the composition consists essentially of a major amount of water, a minor amount of an amine catalyst, a minor amount of an organic surfactant and a minor amount of the siloxane block copolymer.
 7. A composition as defined in claim 6 wherein R is a methyl radical.
 8. A composition as defined in claim 6 wherein R and R'''' are methyl radicals, Z is 1, y is 2 to 6 inclusive, a is 2 to 3 inclusive, and b is 3 to 10 inclusive.
 9. A composition as defined in claim 6 wherein the organic surfactant has the formula C9H19C6H4(OC2H4)10.5OH.
 10. A composition as deFined in claim 6 wherein the siloxane block copolymer has the formula Me3SiO(Me2SiO)2(MeO(C2H4O)3C2H4SiMeO)2.8SiMe3 